The solvothermal synthesis for nanocrystalline FeIn2S4 at low temperature

Citation
Qy. Lu et al., The solvothermal synthesis for nanocrystalline FeIn2S4 at low temperature, CHEM LETT, (6), 1999, pp. 481-482
Citations number
14
Language
INGLESE
art.tipo
Article
Categorie Soggetti
Chemistry
Journal title
CHEMISTRY LETTERS
ISSN journal
0366-7022 → ACNP
Issue
6
Year of publication
1999
Pages
481 - 482
Database
ISI
SICI code
0366-7022(199906):6<481:TSSFNF>2.0.ZU;2-2
Abstract
5 nm thiospinel FeIn2S4 nanocrystallines were prepared through a solvotherm al process at 280 degrees C. Powder X-ray diffraction (XRD) and transmissio n electron microscopy (TEM) reveal that the product was nanocrystalline FeI n2S4 with cubic cell, and uniform spherical particle morphology. The factor s to the formation of uniform FeIn2S4 nanocrystallines with a narrow size d istribution were discussed also.