Citation: Ig. Wright et al., APPLICATION OF A DISPERSED-RESERVOIR CONCEPT FOR THE DEVELOPMENT OF OXIDATION-RESISTANT ALLOYS, Corrosion science, 35(5-8), 1993, pp. 841-854
Citation: A. Strawbridge et al., THE FORMATION AND INCORPORATION INTO THE SCALE OF INTERNAL OXIDES DEVELOPED DURING THE HIGH-TEMPERATURE OXIDATION OF DILUTE NICKEL-BASE ALLOYS, Corrosion science, 35(5-8), 1993, pp. 855-862
Citation: Lv. Ramanathan, ROLE OF RARE-EARTH ELEMENTS ON HIGH-TEMPERATURE OXIDATION BEHAVIOR OFFE-CR, NI-CR AND NI-CR-AL ALLOYS, Corrosion science, 35(5-8), 1993, pp. 871-878
Citation: T. Amano et O. Momose, THE CYCLIC OXIDATION OF NI-20CR ALLOYS WITH SMALL ADDITIONS OF CERIUMAND SILICON, Corrosion science, 35(5-8), 1993, pp. 885-891
Citation: G. Bonnet et al., THE EFFECT OF RARE-EARTHS DEPOSITED ON STEEL SURFACES, BY DIFFERENT PROCESSES (SOL-GEL, ELECTROPHORESIS, OMCVD), ON HIGH-TEMPERATURE CORROSION BEHAVIOR, Corrosion science, 35(5-8), 1993, pp. 893-899
Authors:
CLEMENDOT F
GRAS JM
VANDUYSEN JC
ZACHARIE G
Citation: F. Clemendot et al., INFLUENCE OF YTTRIUM AND METHOD OF FABRICATION ON THE OXIDATION BEHAVIOR OF FE-CR-AL ALLOYS AT HIGH-TEMPERATURE IN AIR, Corrosion science, 35(5-8), 1993, pp. 901-908
Citation: Mw. Johnston et Ja. Little, OXIDATION AND LIQUID ALUMINUM DEGRADATION OF A NITRIDE-BONDED SILICON-CARBIDE CERAMIC, Corrosion science, 35(5-8), 1993, pp. 931-938
Citation: Y. Bhida et H. Anada, THE INFLUENCE OF TERNARY ELEMENT ADDITION ON THE OXIDATION BEHAVIOR OF TIAL INTERMETALLIC COMPOUND IN HIGH-TEMPERATURE AIR, Corrosion science, 35(5-8), 1993, pp. 945-953
Citation: Mm. Nagl et al., THE TENSILE FAILURE OF NICKEL-OXIDE SCALES AT AMBIENT AND AT GROWTH TEMPERATURE, Corrosion science, 35(5-8), 1993, pp. 965-977
Citation: Am. Huntz et al., THE DETERMINATION OF STRESSES DURING OXIDATION OF NI - IN-SITU MEASUREMENTS BY XRD AT HIGH-TEMPERATURE, Corrosion science, 35(5-8), 1993, pp. 989-997
Citation: He. Evans et Rc. Lobb, THE INFLUENCE ON OXIDE SPALLATION OF ANNEALING PERIODS DURING A COOLING CYCLE, Corrosion science, 35(5-8), 1993, pp. 999-1005
Citation: Dm. Rishel et al., SPALLING TYPES AND MECHANISMS IN THE EROSION-CORROSION OF METALS AT HIGH-TEMPERATURE, Corrosion science, 35(5-8), 1993, pp. 1007-1013
Citation: Mm. Stack et Fh. Stott, AN APPROACH TO MODELING EROSION-CORROSION OF ALLOYS USING EROSION-CORROSION MAPS, Corrosion science, 35(5-8), 1993, pp. 1027-1034
Citation: Jgc. Nava et al., THE EFFECT OF SUBSTRATE HARDNESS ON THE EROSION-CORROSION RESISTANCE OF MATERIALS IN LOW-VELOCITY CONDITIONS, Corrosion science, 35(5-8), 1993, pp. 1045-1051